About |
---|
DuPont™ Elvaloy® HP661 is a ethylene terpolymer, which is most commonly used as a modifier for a variety of other polymers. E/nBA/CO = ethylene/n-butyl acrylate/carbon monoxide&& |
Product Description | |
---|---|
Supplier | DOW |
Generic | 热塑性聚酯 |
Material Status | Commercial: Active |
Availabilitys | North America,Europe |
Technical Data | |||
---|---|---|---|
PHYSICAL | Nominal value | Unit | Test method |
Density | 0.960 | g/cm³ | ASTM D792 |
Density | 0.960 | g/cm³ | ISO 1183 |
Melt Flow Rate | |||
190℃,2.16kg | 12 | g/10min | ASTM D1238 |
190℃,2.16kg | 12 | g/10min | ISO 1133 |
MECHANICAL | Nominal value | Unit | Test method |
---|---|---|---|
Shore hardness | 69 | ISO 868 | |
Shaw’s A | 69 | ASTM D2240 | |
tensile strength | |||
fracture | 3.40 | MPa | ASTM D638 |
fracture | 3.40 | MPa | ISO 527-2 |
Tensile strain | |||
fracture | 1100 | % | ISO 527-2 |
fracture | 1100 | % | ASTM D638 |
THERMAL | Nominal value | Unit | Test method |
---|---|---|---|
Glass transition temperature | -54.0 | ℃ | ASTM E1356 |
Melting peak temperature | 62.0 | ℃ | ASTM D3418 |
Melting temperature | |||
DSC | 62.0 | ℃ | ISO 3146 |
Notes |
---|
1. Typical properties: these are not to be construed as specifications. |
2. loss modulus peak at 1 hz |
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |