| DuPont™ Elvax® 3176 is an extrudable ethylene-vinyl acetate copolymer resin available in pellet form for use in conventional extrusion equipment designed to process polyethylene resins. Composition 18 % By Weight Vinyl Acetate comonomer content Chill Roll Release additive, Slip additive Thermal Stabilizer: BHT antioxidant, Applications This resin is designed to provide a low temperature heat seal to itself or many other materials commonly used in flexible packaging applications. The melt properties of this resin allow it to be processed on extrusion coating and cast film equipment over a wide range of line speeds and film thicknesses. Typically, cast film of this grade is adhesive laminated to polyester or other substrates as required by the application.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | EVA |
| Material Status | Commercial: Active |
| Features | Good flexibility,Good heat sealing,Smoothness,Food contact compliance,Inoxidizability,Copolymer,Heat Stabilized,Low temperature heat sealing |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.940 | g/cm³ | ASTM D792 |
| Density | 0.940 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 30 | g/10min | ISO 1133 |
| 190℃，2.16kg | 30 | g/10min | ASTM D1238 |
| Vinyl acetate content | 18.0 | wt% | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 54.0 | ℃ | ASTM D1525 |
| Vicat Softening Temp | 54.0 | ℃ | ISO 306 |
| Melting peak temperature | 84.0 | ℃ | ASTM D3418 |
| Melting temperature | |||
| DSC | 84.0 | ℃ | ISO 3146 |
| freezing point | |||
| — | 61 | ℃ | ISO 3146 |
| — | 61 | ℃ | ASTM D3418 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | < 230 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. DSC |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |