| About |
|---|
| EMERGE™ PC 8600ECO-10 Advanced Resin contains 50% post consumer recycled (PCR) polycarbonate complying with IEEE 1680:2006 certified by TÜV Rheinland. It is a translucent and ignition resistant polycarbonate that does not contain chlorine, bromine, or phosphate additives to comply with global environmental standards. This resin combines good mechanical, thermal, and chemical properties while retaining excellent processability. Applications Electronics and electrical appliances Charges and adaptors enclosures Information technology equipment&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Halogen free,Flame Characteristics,V-2,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 10 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 3.20 mm, injection molded | 2800 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| Yield, 3.20 mm, injection molding | 61.0 | MPa | ASTM D638 |
| Fracture, 3.20 mm, injection molded | 66.0 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| Yield, 3.20 mm, injection molding | 5.0 | % | ASTM D638 |
| Fracture, 3.20 mm, injection molded | 120 | % | ASTM D638 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 810 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 127 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 125 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| — | 149 | ℃ | ASTM D1525 2 |
| — | 150 | ℃ | ISO 306/A120 |
| Ball pressure temperature | > 125 | ℃ | IEC 60335-1 |
| Relative temperature index | 125 | ℃ | UL 746 |
| Electrical performance | 125 | ℃ | UL 746 |
| Impact mechanical performance | 125 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.55 mm | V-2 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| 2.50 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 270 to 300 | °C | |
| Mold temperature | 80 to 110 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Rate B (120°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |