| EMERGE™ PC 4202 advanced resin is 20% glass reinforced polycarbonate containing mold release for optimal processing. This resin exhibits high modulus and excellent dimensional stability. It is available in 8 and 15 Melt Flow Rates. EMERGE PC 4202 resin is typically used in injection molding applications. Applications are information technology equipment, electrical parts, other structural/internal parts.&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Dimensional Stability,V-2,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 8.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.20 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 110 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, annealed | 148 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 138 | ℃ | ASTM D648 |
| 1.8 MPa, annealed | 142 | ℃ | ASTM D648 |
| Vicat Softening Temp | 159 | ℃ | ASTM D1525 2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | V-2 | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| Extreme oxygen index | 30 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 122 | ASTM D785 | |
| Tensile modulus | 5170 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| yield | 82.7 | MPa | ASTM D638 |
| fracture | 82.7 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 3.0 | % | ASTM D638 |
| Bending modulus | 4960 | MPa | ASTM D790 |
| bending strength | 148 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Melt temperature (target) | 288 | °C | |
| Mold temperature | 82 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Rate A (50°C/h), Loading 2 (50 N) |
| 3. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |