| EMERGE™ PC 4310-22 Advanced Resin is a high-performance polycarbonate resin offering high heat resistance, toughness, and superior flow. This resin is available in a full range of colors that can be custom tailored to meet your product requirements. Applications: Consumer Electronics and Information Technology Equipment Computer and Business Equipment Portable Electronics&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good flexibility,High liquidity,High Heat Resistance,HB |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 22 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 750 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23 ℃, 3.2 mm, injection molding | 无断裂 | ASTM D256 | |
| Dart impact equipped with measuring instruments | |||
| 23 ℃, 3.20 mm, injection molding, peak energy | 72.3 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, annealed, 4.0 mm | 142 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.99 mm | 126 | ℃ | ASTM D648 |
| 1.8 MPa, annealed, 4.0 mm | 139 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD：-40~80℃ | 6.8E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 2.0E+17 | ohms·cm | ASTM D257 |
| Dielectric strength | 17 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 60 Hz | 3.00 | ASTM D150 | |
| 1 MHz | 3.00 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 60 Hz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 2.0E-3 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 | |
| Extreme oxygen index | 26 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-grade, 3.20 mm | 118 | ASTM D785 | |
| Tensile modulus | |||
| 3.20 mm, injection molded | 2340 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| Yield, 3.20 mm, injection molding | 60.0 | MPa | ASTM D638 |
| Fracture, 3.20 mm, injection molded | 65.5 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm, injection molded | 120 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm, injection molded | 2410 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm, injection molded | 96.5 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 260 to 277 | °C | |
| Mold temperature | 71 to 93 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 11.1 ft/sec |
| 3. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |