| EMERGE™ 4314 (former name XQR 70107.02) Advanced Resin is a 40% Glass Filled PC resin that is colored to either high reflective white or black color. It provides a property balance of high flowability, low dimensional distortion and high stiffness that can meet the market needs of thin wall application with high heat requirement. Applications: Handheld devices Electronic accessories&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,High liquidity,High Heat Resistance |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.54 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 16 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.040 to 0.070 | % | |
| TD | 0.15 to 0.23 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 3.20 mm, injection molded | 9800 | MPa | ASTM D638 |
| tensile strength | |||
| Fracture, 3.20 mm, injection molded | 132 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm, injection molded | 1.4 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm, injection molded | 9900 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm, injection molded | 178 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 89 | J/m | ASTM D256 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 115 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 270 to 310 | °C | |
| Mold temperature | 70 to 90 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |