| About |
|---|
| EMERGE™ PC 8080-15 advanced resin is an opaque, ignition resistant PC resin that contains no chlorinated or brominated or phosphorous based additives. This resin contains mould release and it is UV stabilized. It combines good mechanical and high heat properties and maintains excellent processability. EMERGE™ PC 8080-15 has a UL 94 V-0 rating at 0.7 mm. Applications: Electrical Electronics&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,Halogen free,Flame Characteristics,High Heat Resistance,Low to no phosphorus content |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183/B |
| Melt Flow Rate | |||
| 300℃，1.20kg | 15 | g/10min | ISO 1133 |
| Shrinkage rate | 0.50 to 0.70 | % | ISO 294-4 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 25 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 65 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, annealed | 142 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 123 | ℃ | ISO 75-2/A |
| 1.8 MPa, annealed | 139 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 146 | ℃ | ISO 306 |
| Ball pressure temperature | > 125 | ℃ | IEC 60335-1 |
| Linear coefficient of thermal expansion | |||
| MD | 7.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 17 | kV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 1 Hz | 2.70 | ||
| 50 Hz | 2.70 | ||
| Dissipation factor | |||
| 1 Hz | 1.0E-3 | ||
| 50 Hz | 1.0E-3 | ||
| Compared to the leakage tracing index | |||
| Solution A | 225 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.70 mm | V-0 | ||
| 2.00 mm | 5VB | ||
| 2.50 mm | 5VA | ||
| Glowing wire flammability index | |||
| 1.0 mm | 960 | ℃ | |
| 2.0 mm | 960 | ℃ | |
| 3.0 mm | 960 | ℃ | |
| Igniting temperature of the hot wire | |||
| 1 mm | 850 | ℃ | |
| 2 mm | 850 | ℃ | |
| 3 mm | 850 | ℃ | |
| Extreme oxygen index | 40 | % | ISO 4589-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 73 | ||
| R-level | 118 | ||
| Tensile modulus | 2400 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 62.0 | MPa | |
| fracture | 60.0 | MPa | |
| Tensile strain | |||
| fracture | 110 | % | ISO 527-2/50 |
| Bending modulus | 2350 | MPa | ISO 178 |
| bending strength | 95.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 260 to 300 | °C | |
| Mold temperature | 70 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |