| About |
|---|
| Emerge™ 8210-22 advanced resin is an opaque, ignition resistant PC resin that contains no chlorinated or brominated or phosphorous based additives. This resin combines good mechanical and high heat properties, maintains excellent processability and contains mold release agent. Emerge 8210-22 has a UL94 V0 rating at 1.5mm. Applications: A broad range of injection molded applications in the lighting, electronics, electrical and information technology equipment markets.&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Halogen free,Flame Characteristics,High Heat Resistance,V-0 |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183/B |
| Melt Flow Rate | |||
| 300℃，1.20kg | 22 | g/10min | ISO 1133 |
| Shrinkage rate | 0.50 to 0.70 | % | ISO 294-4 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 20 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 60 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, annealed | 140 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 123 | ℃ | ISO 75-2/A |
| 1.8 MPa, annealed | 137 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 143 | ℃ | ISO 306 |
| Ball pressure temperature | > 125 | ℃ | IEC 60335-1 |
| Linear coefficient of thermal expansion | |||
| MD | 7.0E-5 | 1/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 5VA | UL 94 | |
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 1.0 mm | 960 | ℃ | IEC 60695-2-12 |
| 2.0 mm | 960 | ℃ | IEC 60695-2-12 |
| 3.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 1 mm | 800 | ℃ | IEC 60695-2-13 |
| 2 mm | 800 | ℃ | IEC 60695-2-13 |
| 3 mm | 800 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 40 | % | ISO 4589-2 |
| Needle flame test | |||
| 1.50 mm | PASS | IEC 60695-2-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | ||
| M-level | 73 | ISO 2039-2 | |
| R-level | 118 | ISO 2039-2 | |
| Tensile modulus | 2400 | MPa | ISO 527-1-2 |
| tensile strength | ISO 527-2/50 | ||
| yield | 60.0 | MPa | ISO 527-2/50 |
| fracture | 58.0 | MPa | ISO 527-2/50 |
| Tensile strain | ISO 527-2/50 | ||
| yield | 6.0 | % | ISO 527-2/50 |
| fracture | 100 | % | ISO 527-2/50 |
| Bending modulus | 2350 | MPa | ISO 178 |
| bending strength | 95.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 260 to 300 | °C | |
| Mold temperature | 70 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |