| EMERGE™ PC 8600 is a translucent, ignition-resistant and easy flow polycarbonate resin. This resin contains no bromine, chlorine or phosphate additives and is intended to comply with global environmental standards. It has a UL94 flammability rating of V-0 at 1.5mm. Applications: A broad range of injection molded applications in the electronics, electrical and information technology equipment markets.&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good liquidity,Halogen free,Flame Characteristics,V-0 |
| Availabilitys | North America,Latin America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183/B |
| Melt Flow Rate | |||
| 300℃，1.20kg | 20 | g/10min | ISO 1133 |
| Shrinkage rate | 0.50 to 0.70 | % | ISO 294-4 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, injection molding | 690 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 122 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 136 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| — | 150 | ℃ | ISO 306/A120 |
| B50 | 143 | ℃ | ISO 306 |
| Ball pressure temperature | > 125 | ℃ | IEC 60335-1 |
| Linear coefficient of thermal expansion | |||
| MD：-40~82℃ | 6.5E-5 | 1/℃ | ASTM D696 |
| Relative temperature index | |||
| Electrical performance | 125 | ℃ | UL 746 |
| Strength mechanical performance | 125 | ℃ | UL 746 |
| Impact mechanical performance | 125 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 | |
| Igniting temperature of the hot wire | |||
| 1 mm | 960 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 35 | % | ISO 4589-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 4 mm, injection molded | 58.0 | MPa | ISO 527-2/50 |
| Yield, 4 mm, injection molding | 60.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Fracture, 4 mm, injection molded | 100 | % | ISO 527-2/50 |
| Yield, 4 mm, injection molding | 6.0 | % | ISO 527-2/50 |
| Bending modulus | |||
| 4 mm, injection molded | 2400 | MPa | ISO 178 |
| bending strength | |||
| 4 mm, injection molded | 94.0 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-grade, 4.00 mm | 123 | ISO 2039-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 125 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 260 to 280 | °C | |
| Mold temperature | 70 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |