| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Negative |
| Features | Good liquidity,Flame Characteristics,Halogen free,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 9.0 | g/10min | ASTM D1238 |
| Molding shrinkage | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield yld | 60 | MPa | ASTM D638 |
| Broken BRK | 65 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield yld | 6 | % | ASTM D638 |
| Broken BRK | 120 | % | ASTM D638 |
| Flexural Modulus | 2400 | MPa | ASTM D790 |
| Flexural Strength | 95 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod Notched Impact strength | 750 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, unannealed | 126 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 125 | ℃ | ISO 75-1/-2 |
| Vicat Softening Temperature | 150 | ℃ | ASTM D1525 |
| Ball Pressure Test | >125 | ℃ | IEC 60335-1 |
| Coeff. of linear thermal expansion | |||
| -40℃-80℃ | 6.5E-5 | cm/cm/℃ | ASTM D696 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume Resistance | 1E17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 22 | kV/mm | ASTM D149 |
| Arc Resistance | PLC 7 | ASTM D495 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 0.4 mm | HB | UL 94 | |
| 0.55 mm | V-2 | UL 94 | |
| 1.0 mm | V-1 | UL 94 | |
| 1.5 mm | V-0 | UL 94 | |
| 2.5 mm | V-0 | UL 94 | |
| 3.0 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index (GWFI) | |||
| 2.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature (GWIT) | |||
| 2.0 mm | 800 | ℃ | IEC 60695-2-13 |
| Oxygen Index | 35 | % | ISO 4589-2 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Melt Temperature | 270 to 300 | °C | |
| Mold Temperature | 70 to 110 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |