| About |
|---|
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,Moderate liquidity,V-0 |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.33 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 9.98 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.3-0.6 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 3.20 mm, injection molded | 6400 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 3.20 mm, injection molding | 100 | MPa | ASTM D638 |
| Fracture, 3.20 mm, injection molded | 100 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm, injection molded | 3.5 | % | ASTM D638 |
| Yield, 3.20 mm, injection molding | 3.5 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm, injection molded | 6500 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm, injection molded | 150 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 105 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 1.8 MPa, unannealed | 134 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | |||
| 1.1GHz | 3.06 | EC 17025 | |
| 2.4GHz | 3.06 | EC 17025 | |
| 5.0GHz | 3.06 | EC 17025 | |
| Dissipation factor | |||
| 1.1GHz | 0.0070 | EC 17025 | |
| 2.4GHz | 0.0061 | EC 17025 | |
| 5.0GHz | 0.0061 | EC 17025 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 | |
| 0.75 mm | V-2 | UL 94 | |
| 0.4 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 115-125 | °C | |
| Drying time | 3.0-4.0 | hrs | |
| Processing (melt) temperature | 288-310 | °C | |
| Mold temperature | 80-110 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |