| EMERGE™ PC/ABS 7100 advanced resin exhibits a balance of properties between impact strength, heat resistance and processability. Its superior natural base color and lot-to-lot color consistency makes it ideally suited for producing very consistent colored parts. It has excellent flow and is ideal for injection molding in thin-wall applications, such as portable electronic devices.&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,High liquidity,High Heat Resistance,HB |
| Availabilitys | North America,Latin America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.11 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 230℃，3.80kg | 4.5 | g/10min | ASTM D1238 |
| 260℃，5.0kg | 25 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30 ℃, 3.2mm, injection molding | 290 | J/m | ASTM D256 |
| 23 ℃, 3.2mm, injection molding | 480 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.2 mm, injection molded | 116 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm, injection molded | 95.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 133 | ℃ | ASTM D1525 4 |
| Linear coefficient of thermal expansion | |||
| MD | 7.6E-5 | 1/℃ | ASTM D696 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.00 mm | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| drying temperature |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-grade, 3.20 mm | 112 | ASTM D785 | |
| Tensile modulus | |||
| 3.20 mm, injection molded | 2210 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 3.20 mm, injection molding | 50.3 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| Yield, 3.20 mm, injection molding | 4.0 | % | ASTM D638 |
| Fracture, 3.20 mm, injection molded | 50 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm, injection molded | 2340 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm, injection molded | 80.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 238 to 266 | °C | |
| Mold temperature | 49 to 91 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Rate B (120°C/h), Loading 1 (10 N) |
| 4. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |