| About |
|---|
| EMERGE™ PC/ABS 7502 is a non-halogen ignition resistant 20% glass filled PC/ABS resin. It combines the superior physical properties of PC and the excellent processability of ABS. EMERGE PC/ABS 7502 is designed with excellent flow and high rigidity, outstanding capability in chemical resistance for use in internal structural parts of OA machine particular those, parts with thin wall thickness.&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,High liquidity,Halogen free,Flame Characteristics,Solvent resistance,V-2,V-1,V-0,5VA |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.33 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 17 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.15 to 0.30 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 5200 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 101 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.8 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm, injection molded | 6200 | MPa | ASTM D790 |
| bending strength | 155 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 380 | J/m | ASTM D256 |
| 23 ℃, 3.2mm, injection molding | 110 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 110 | ℃ | ASTM D648 |
| Vicat Softening Temp | 112 | ℃ | ASTM D1525 2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.50 mm | V-2 | UL 94 | |
| 1.00 mm | V-1 | UL 94 | |
| 1.20 mm, black, white | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| 2.00 mm | 5VA | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Barrel rear temperature | 240 to 250 | °C | |
| Barrel middle temperature | 250 to 270 | °C | |
| Barrel front temperature | 250 to 270 | °C | |
| Nozzle temperature | 270 to 290 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Rate A (50°C/h), Loading 2 (50 N) |
| 3. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |