| About |
|---|
| EMERGE™ PC/ABS 7530 advanced resin is a high flow, ignition-resistant PC/ABS blend that contains no chlorine or bromine flame retardants. It has good property balance of flow ability, impact and heat stability. It is suitable for the injection molding for large, thin-wall and Intricate parts. It can be used in a wide variety of applications in the Information Technology Equipment and Consumer Electronics Industries Applications: Notebook & Desktop Computer Enclosures TV & monitor enclosures Power Adaptors and Chargers&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | High liquidity,Halogen free,Flame Characteristics,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.17 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 230℃，3.80kg | 16 | g/10min | ASTM D1238 |
| 260℃，5.0kg | 70 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.60 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 640 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 95.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 82.8 | ℃ | ASTM D648 |
| Vicat Softening Temp | 108 | ℃ | ASTM D1525 3 |
| Ball pressure temperature | 90.0 | ℃ | IEC 60335-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 | |
| Glowing wire flammability index | |||
| 2.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 2 mm | 925 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 29 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-grade, 3.20 mm | 120 | ASTM D785 | |
| tensile strength | ASTM D638 | ||
| Yield, 3.20 mm, injection molding | 62.1 | MPa | ASTM D638 |
| Fracture, 3.20 mm, injection molded | 45.5 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| Yield, 3.20 mm, injection molding | 4.0 | % | ASTM D638 |
| Fracture, 3.20 mm, injection molded | 60 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm, injection molded | 2830 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm, injection molded | 97.9 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 79 to 91 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 230 to 260 | °C | |
| Mold temperature | 60 to 91 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Rate B (120°C/h), Loading 1 (10 N) |
| 3. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |