| About |
|---|
| EMERGE™ PC/ABS 7570 Advanced Resin is a high flow, ignition-resistant PC/ABS blend that contains no chlorinated or brominated additives. Its superior processing makes it ideal for injection molding of large, thin-wall, or intricate parts. EMERGE PC/ABS 7570 is suitable for use in a wide variety of applications in the Information Technology Equipment & Consumer Electronics industries. Applications: LCD TV Enclosures CRT TV Enclosures Monitor and PC Enclosures&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | High liquidity,Halogen free,Flame Characteristics,V-0 |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ISO 1183/B |
| Apparent density | 0.67 | g/cm³ | ISO 60 |
| Melt Flow Rate | ISO 1133 | ||
| 230℃，3.80kg | 20 | g/10min | ISO 1133 |
| 260℃，5.0kg | 95 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.40 to 0.60 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 4 mm, injection molded | 2600 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Fracture, 4 mm, injection molded | 47.0 | MPa | ISO 527-2/50 |
| Yield, 4 mm, injection molding | 60.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Fracture, 4 mm, injection molded | 40 | % | ISO 527-2/50 |
| Yield, 4 mm, injection molding | 4.0 | % | ISO 527-2/50 |
| Bending modulus | |||
| 4 mm, injection molded | 2700 | MPa | ISO 178 |
| bending strength | |||
| 4 mm, injection molded | 92.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 18 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 12 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 80.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 90.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| — | 105 | ℃ | ISO 306/A120 |
| B50 | 98.0 | ℃ | ISO 306 |
| Ball pressure temperature | 95.0 | ℃ | IEC 60335-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm, all colors | V-0 | UL 94 | |
| 2.50 mm, natural color | V-0 | UL 94 | |
| Glowing wire flammability index | |||
| 2.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 2 mm | 800 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 240 to 280 | °C | |
| Mold temperature | 40 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |