| About |
|---|
| EMERGE 7590ECO Advanced Resin is an ignition-resistance PC/ABS alloy containing 35% post consumer recycled (PCR) materials and no chlorine or bromine additives. This resin provides superior processability for molding thin-wall parts and optimizing cycle time productivity in injection molding operations. Applications: Enclosures for consumer electronics Accessories in information technology equipment&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Halogen free,Flame Characteristics,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.21 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 15 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.60 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 3.20 mm, injection molded | 2420 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| Yield, 3.20 mm, injection molding | 55.0 | MPa | ASTM D638 |
| Fracture, 3.20 mm, injection molded | 46.0 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| Yield, 3.20 mm, injection molding | 4.0 | % | ASTM D638 |
| Fracture, 3.20 mm, injection molded | 100 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm, injection molded | 2830 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm, injection molded | 97.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 720 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23 ℃, 3.2 mm, injection molding | 无断裂 | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 82.0 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | Internal Method | |
| Extreme oxygen index | 29 | % | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 220 to 250 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |