| About |
|---|
| EMERGE™ PC/ABS 7700 Advanced Resin is an ignition-resistant PC/ABS blend that contains no chlorine or bromine additives. It has superior processability for injection molding applications. This grade has excellent aesthetics, is UV stabilized and is available in custom colors. Main Characteristics: Tested under ISO 10993 (Parts 5 & 10) RoHS Compliant Applications: Medical equipment housings Consumer Electronics Information technology equipment&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,Good surface appearance,High impact resistance,Halogen free,Flame Characteristics,V-0,5VA,5VB |
| Availabilitys | North America,Latin America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.17 | g/cm³ | ASTM D792 |
| Density | 1.18 | g/cm³ | ISO 1183/B |
| Melt Flow Rate | |||
| 230℃，3.80kg | 11 | g/10min | ASTM D1238 |
| 240℃，5.0kg | 20 | g/10min | ASTM D1238 |
| 260℃，2.16kg | 13 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.40 to 0.60 | % | ISO 294-4 |
| MD | 0.40 to 0.60 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30 ℃, injection molding | 15 | kJ/m² | ISO 179/1eA |
| 23 ℃, injection molding | 40 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -18 ℃, 3.2mm, injection molding | 200 | J/m | ASTM D256 |
| -7℃ | 440 | J/m | ASTM D256 |
| 23 ℃, 3.2mm, injection molding | 480 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/A | ||
| -30 ℃, injection molding | 14 | kJ/m² | ISO 180-A |
| 23 ℃, injection molding | 50 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 77.0 | ℃ | ISO 75-2/A |
| 1.8 MPa, unannealed | 79.4 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 90.6 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 88.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 104 | ℃ | ASTM D1525 2 |
| Vicat Softening Temp | |||
| — | 104 | ℃ | ISO 306/A120 |
| B50 | 94.0 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 6.8E-5 | 1/℃ | ASTM D696 |
| MD：-40~40℃ | 6.8E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 5.2E+15 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+18 | ohms·cm | IEC 60093 |
| Dielectric strength | IEC 60243-1 | ||
| 1.6 mm in oil | 26 | kV/mm | IEC 60243-1 |
| 3.2 mm in oil | 18 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 100 Hz | 2.86 | IEC 60250 | |
| 1 MHz | 2.80 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 4.0E-3 | IEC 60250 | |
| 1 MHz | 7.0E-3 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 2.00 mm | 5VB | UL 94 | |
| 2.50 mm | 5VA | UL 94 | |
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 1.5 mm | 925 | ℃ | IEC 60695-2-12 |
| 2.0 mm | 925 | ℃ | IEC 60695-2-12 |
| 2.5 mm | 925 | ℃ | IEC 60695-2-12 |
| 3.0 mm | 950 | ℃ | IEC 60695-2-12 |
| Extreme oxygen index | 28 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 4 mm, injection molded | 2560 | MPa | ISO 527-1-2 |
| 3.20 mm, injection molded | 2620 | MPa | ASTM D638 |
| tensile strength | |||
| Fracture, 4 mm, injection molded | 45.0 | MPa | ISO 527-2/50 |
| Fracture, 3.20 mm, injection molded | 48.3 | MPa | ASTM D638 |
| Yield, 4 mm, injection molding | 55.0 | MPa | ISO 527-2/50 |
| Yield, 3.20 mm, injection molding | 60.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 4 mm, injection molded | 43 | % | ISO 527-2/50 |
| Fracture, 3.20 mm, injection molded | 65 | % | ASTM D638 |
| Yield, 4 mm, injection molding | 3.8 | % | ISO 527-2/50 |
| Yield, 3.20 mm, injection molding | 3.8 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm, injection molded | 2690 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm, injection molded | 96.5 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-grade, 3.20 mm | 120 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 to 88 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 238 to 274 | °C | |
| Mold temperature | 60 to 91 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Rate B (120°C/h), Loading 1 (10 N) |
| 3. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |