| About |
|---|
| EMERGETM PC/ABS 7800 Advanced Resin is an ignition-resistance PC/ABS blend that contains no chlorine or bromine additives. It contains up to 40% of post consumer recycle (PCR) polycarbonate. This resin is suitable for use in a wide variety of applications in the information technology equipment and consumer electronics markets. Applications TV enclosures Monitor enclosures Laptop and desktop computer housing Computer peripherals&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,V-0 |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 12 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.60 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 60.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 50 | % | ASTM D638 |
| Bending modulus | 2620 | MPa | ASTM D790 |
| bending strength | 84.8 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 640 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 92.2 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 81.1 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.70 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Mold temperature | 40 to 60 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |