About |
---|
EMERGE* 7880ECO PC/ABS Advanced Resin is an ignition-resistance PC/ABS blend that contains no chlorine or bromine additives. It contains up to 50% of post consumer recycle (PCR). This resin is suitable for use in a wide variety of applications in the information technology equipment and consumer electronics markets. Applications: Computer peripherals&& |
Product Description | |
---|---|
Supplier | Trinseo |
Generic | PC+ABS |
Material Status | Commercial: Active |
Features | Halogen free,Flame Characteristics,V-2,V-0 |
Availabilitys | Asia Pacific |
Process Methods | Injection Molding |
Technical Data | |||
---|---|---|---|
PHYSICAL | Nominal value | Unit | Test method |
Density | 1.18 | g/cm³ | ASTM D792 |
Melt Flow Rate | ASTM D1238 | ||
230℃,3.80kg | 10 | g/10min | ASTM D1238 |
260℃,2.16kg | 15 | g/10min | ASTM D1238 |
Shrinkage rate | |||
MD | 0.50 to 0.70 | % | ASTM D955 |
MECHANICAL | Nominal value | Unit | Test method |
---|---|---|---|
tensile strength | |||
yield | 60.0 | MPa | ASTM D638 |
Tensile strain | |||
fracture | 60 | % | ASTM D638 |
Bending modulus | 2500 | MPa | ASTM D790 |
bending strength | 88.3 | MPa | ASTM D790 |
IMPACT | Nominal value | Unit | Test method |
---|---|---|---|
Impact strength of cantilever beam notch | |||
23℃ | 720 | J/m | ASTM D256 |
THERMAL | Nominal value | Unit | Test method |
---|---|---|---|
Hot deformation temperature | |||
1.8 MPa, unannealed | 80.0 | ℃ | ASTM D648 |
Vicat Softening Temp | 102 | ℃ | ASTM D1525 3 |
Electrical performance | Nominal value | Unit | Test method |
---|---|---|---|
Volume resistivity | 11 | ohms·cm | ASTM D257 |
Dielectric strength | 20 | kV/mm | ASTM D149 |
Compared to the leakage tracing index | > 600 | V | IEC 60112 |
FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
---|---|---|---|
Flame retardant level | UL 94 | ||
0.50 mm | V-2 | UL 94 | |
1.00 mm | V-0 | UL 94 | |
2.00 mm | 5VB 5VB | UL 94 | |
Glowing wire flammability index | |||
0.50 mm | 960 | ℃ | IEC 60695-2-12 |
Process Conditions | |||
---|---|---|---|
injection | Nominal value | Unit | Test method |
Drying temperature | 80 | °C | |
Drying time | 3.0 to 4.0 | hr | |
Processing (melt) temperature | 238 to 266 | °C | |
Mold temperature | 50 to 74 | °C |
Notes |
---|
1. Typical properties: these are not to be construed as specifications. |
2. Rate B (120°C/h), Loading 2 (50 N) |
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |