| About |
|---|
| EMERGE™ PC/PET 9100CR advanced resin is a polycarbonate blend with excellent chemical resistance. This grade was designed for use in medical equipment housings and can withstand repeated exposure to a variety of cleaners and disinfectants commonly used in hospitals. This grade has good aesthetics and excellent toughness. Main Characteristics: Excellent chemical resistance Tested under ISO 10993 UL listing for HB Applications: Medical device housings or enclosures&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PC+PET |
| Material Status | Commercial: Active |
| Features | Good flexibility,Good surface appearance,Biocompatible,Solvent resistance,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.23 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 8.5 | g/10min | ASTM D1238 |
| Shrinkage rate | ASTM D955 | ||
| MD | 0.60 to 0.90 | % | ASTM D955 |
| TD | 0.50 to 0.80 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30 ℃, 3.2mm, injection molding | 750 | J/m | ASTM D256 |
| 23 ℃, 3.2mm, injection molding | 910 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -40 ℃, 3.20 mm, injection molded, Peak Energy | 55.4 | J | ASTM D3763 |
| -40 ℃, 3.20 mm, injection molded, Total Energy | 80.2 | J | ASTM D3763 |
| 23 ℃, 3.20 mm, injection molded, Peak Energy | 46.3 | J | ASTM D3763 |
| 23 ℃, 3.20 mm, injection molding, total energy | 63.3 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 117 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 87.2 | ℃ | ASTM D648 |
| Vicat Softening Temp | 144 | ℃ | ASTM D1525 7 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 4.3E+15 | ohms | IEC 60093 |
| Volume resistivity | 3.4E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | IEC 60243-1 | ||
| 1.6 mm in oil | 28 | kV/mm | IEC 60243-1 |
| 3.2 mm in oil | 17 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 100 Hz | 3.28 | IEC 60250 | |
| 1 MHz | 3.12 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 2.0E-3 | IEC 60250 | |
| 1 MHz | 0.020 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.00 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-grade, 3.20 mm | 111 | ASTM D785 | |
| Tensile modulus | |||
| 3.20 mm, injection molded | 2210 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| Yield, 3.20 mm, injection molding | 50.0 | MPa | ASTM D638 |
| Fracture, 3.20 mm, injection molded | 56.2 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| Yield, 3.20 mm, injection molding | 4.7 | % | ASTM D638 |
| Fracture, 3.20 mm, injection molded | 150 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm, injection molded | 2100 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm, injection molded | 77.2 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 249 to 282 | °C | |
| Mold temperature | 43 to 99 | °C | |
| Notes |
|---|
| 1. Biocompatibility testing following ISO Guidelines 10993 has been completed on select classic resins in this series. Please consult Styron for details. ISO guidelines include a sensitization test. |
| 2. Typical properties: these are not to be construed as specifications. |
| 3. 0.20 in/min |
| 4. 2.0 in/min |
| 5. 0.051 in/min |
| 6. Rate B (120°C/h), Loading 1 (10 N) |
| 7. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |