| About |
|---|
| EMPILON® HAR series compound are specially designed for over-molding with engineering plastic such as ABS, PC, Nylon, PETG, PBT etc. which are commonly use in the 3C industry (Computer, Communication and Consumer electronics) as well as hand held device products for soft touch, anti-slip & vibration functional purposes. Hydrogenated Styrenic Block Copolymer is the main content of this HAR series compound, its hardness range is from Shore A 39 ~ Shore 85. They can be processed by double injection and co-extrusion machines or ordinary plastic injection machines with an insert molding process.&& |
| Product Description | |
|---|---|
| Supplier | EMPILON |
| Generic | SEBS |
| Material Status | Commercial: Active |
| Features | Renewable resources,Hydrolysis stability,Halogen free,No antimony,Block Copolymer,Lead content is low to none,Nontoxicity,Low to no calcium content |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 1.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 | % | |
| TD | 0.50 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 10 seconds | 74 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 6.86 | MPa | ASTM D412 |
| 300% strain | 3.43 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 500 | % | ASTM D412 |
| Compression deformation | |||
| 23℃，70 hr | 19 | % | ASTM D395 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | |||
| 125℃，168 hr | 47 | % | ASTM D573 |
| The rate of change in ultimate elongation in air | |||
| 125℃，168 hr | 15 | % | ASTM D573 |
| The rate of change in hardness of a hardness tester in the air | |||
| Shaw A, 125 ℃, 168 hr | 3.0 | ASTM D573 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -40.0 | ℃ |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Adhesion to ABS | 3.9 | kN/m | |
| Adhesion to PC | 3.5 | kN/m |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 2.0 | hr | |
| Barrel rear temperature | 180 to 190 | °C | |
| Barrel middle temperature | 185 to 200 | °C | |
| Barrel front temperature | 195 to 205 | °C | |
| Nozzle temperature | 200 to 220 | °C | |
| Processing (melt) temperature | 190 to 210 | °C | |
| Mold temperature | 40 to 50 | °C | |
| Injection pressure | 3.43 to 4.90 | MPa | |
| Injection speed | 中等 | ||
| Back pressure | 0.490 to 0.981 | MPa | |
| Screw Speed | Medium | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Reference Only |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |