Emulprene® 1006CR

About
Description: E1006CR is a crumb hot emulsion styrene-butadiene copolymer, polymerized using a fatty acid emulsifier and coagulated with salt-acid. It is a very light color product stabilized with a non-staining antioxidant, and presented as free flowing dusted crumb which eliminates the end for size reduction equipment. Between 7% and 12% of Calcium Carbonate is used as dusting agent. Applications: E1006CR is recommended for light colored applications; for adhesives, tire white sidewalls, transport and transmission belts, sponge materials, sporting goods, flooring, colored shoe soles and heels.&&

About

Description: E1006CR is a crumb hot emulsion styrene-butadiene copolymer, polymerized using a fatty acid emulsifier and coagulated with salt-acid. It is a very light color product stabilized with a non-staining antioxidant, and presented as free flowing dusted crumb which eliminates the end for size reduction equipment. Between 7% and 12% of Calcium Carbonate is used as dusting agent. Applications: E1006CR is recommended for light colored applications; for adhesives, tire white sidewalls, transport and transmission belts, sponge materials, sporting goods, flooring, colored shoe soles and heels.&&

Product Description
Generic	SBR-乳液聚合
Material Status	Commercial: Active
Features	The fouling resistance,High liquidity,Inoxidizability,Copolymer
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Mooney viscosity			ASTM D1646
ML 1+4，100℃	45 to 55	MU	ASTM D1646
ML 1+4，100℃	68	MU	ASTM D1646
Organic Acid	4.0 to 6.0	%	ASTM D5774
Soap	< 0.50	%	ASTM D5774
styrene content
Bound	23 to 25	%	ASTM D5775
Ash Content	< 1.0	%	ASTM D5667
Volatiles	< 0.75	%	ASTM D5668

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	15.6	MPa	ASTM D3185
tensile strength	25.0	MPa	ASTM D3185
Tensile strain
fracture	450	%	ASTM D3185

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.