| Description: E1013A is a styrene-butadiene copolymer, hot polymerized using a fatty acid soap. Previously to the alum-acid coagulation, a non-staining stabilizer is added in the manufacturing process. Applications: E1013A is suitable for adhesive applications it is particularly used for can-sealing compounds, tire liners, mechanical goods, including auto mounts, and household products.&& |
| Product Description | |
|---|---|
| Generic | SBR-乳液聚合 |
| Material Status | Commercial: Active |
| Features | The fouling resistance,Good bond,Copolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Mooney viscosity | ASTM D1646 | ||
| ML 1+4，100℃ | 40 to 50 | MU | ASTM D1646 |
| ML 1+4，100℃ | 55 to 65 | MU | ASTM D1646 |
| Organic Acid | 3.5 to 5.5 | % | ASTM D5774 |
| Soap | < 0.30 | % | ASTM D5774 |
| styrene content | |||
| Bound | 42 to 45 | % | ASTM D5775 |
| Ash Content | < 1.0 | % | ASTM D5667 |
| Volatiles | < 1.0 | % | ASTM D5668 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 14.0 to 16.0 | MPa | ASTM D3185 |
| tensile strength | 20.0 to 24.0 | MPa | ASTM D3185 |
| Tensile strain | |||
| fracture | 300 to 500 | % | ASTM D3185 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Compound |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |