| Impact Modified, Molding Grade PC/PBT with UV Stabilizer |
| Product Description | |
|---|---|
| Supplier | EnCom |
| Generic | PC+PBT |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,High impact resistance |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 266℃，5.0kg | 22 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 1.6 to 1.8 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile strength (yield) | 42.7 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 150 | % | ASTM D638 |
| Bending modulus | 1790 | MPa | ASTM D790 |
| bending strength | 62.1 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -30℃ | 640 | J/m | |
| 23℃ | 910 | J/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 98.9 | ℃ | |
| 1.8 MPa, unannealed | 60.0 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 104 to 121 | °C | |
| Drying time | 3.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Temperature at the rear of the barrel | 249 to 282 | °C | |
| Temperature in the middle of the barrel | 254 to 288 | °C | |
| Front temperature of material barrel | 260 to 299 | °C | |
| Nozzle temperature | 274 to 302 | °C | |
| Processing (melt) temperature | 277 to 307 | °C | |
| Mold temperature | 66 to 93 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 40 to 75 | rpm | |
| Exhaust hole depth | 0.038 to 0.076 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |