| About |
|---|
| ENGAGE™ 7447 is a high ethylene butene melt flow, low density copolymer designed for use alone or in combination with our other elastomers to provide the tailored solutions in polymer modifications applications. Main Characteristics: Pellet form Low Density Talc dusted (untreated, 1µm) Applications: Polymer modification Blends Complies with Government / Industry Standards: FDA FCN 368 EU, No 10/2011&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.865 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 5.0 | g/10min | ASTM D1238 |
| Mooney viscosity | |||
| ML 1+4，121℃ | 7 | MU | ASTM D1646 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | 24.8 | kN/m | ASTM D624 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -53.0 | ℃ | Internal Method |
| Melting temperature | |||
| DSC | 35.0 | ℃ | Internal Method |
| Crystallization peak temperature | |||
| DSC | 29.0 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shore A, 1 second, molded | 64 | ASTM D2240 | |
| Shore D, 1 second, molded | 12 | ASTM D2240 | |
| Tensile modulus | |||
| 100% cut, molded | 1.70 | MPa | ASTM D638 |
| tensile strength | |||
| Fracture, molded | 2.40 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, molded | 550 | % | ASTM D638 |
| Bending modulus | ASTM D790 | ||
| 1% cut, molded | 7.80 | MPa | ASTM D790 |
| 2% cut, molded | 7.60 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 20 in/min |
| 3. Die C |
| 4. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |