| About |
|---|
| ENGAGE™ 8003 EL Polyolefin Elastomer is an ethylene-octene copolymer that has excellent flow characteristics and performs well in a wide variety of Wire & Cable elastomer applications. ENGAGE 8003 EL provides superb impact properties and also provides high filler loading capability and outstanding peroxide cure capability. When cross-linked by peroxide, silane, or irradiation, it gives exceptional heat aging, compression set, and weather resistance properties, and may be used to produce high performance electrical insulation and jacketing. Main Characteristics: Pellet form Excellent flow characteristics High filler loading Peroxide, silane, and radiation curable Exceptional heat aging, compression set, and weather resistance when cured Applications: Wire and cable Complies with: EU, No 10/2011 Japan Hygienic Olefin and Styrene Plastics Association NSF/ANSI Standard 51-Food Equipment Materials U.S. FDA 21 CFR 177.1520(c)3.2c&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.885 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ASTM D1238 |
| Mooney viscosity | |||
| ML 1+4，121℃ | 22 | MU | ASTM D1646 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | 61.0 | kN/m | ASTM D624 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -46.0 | ℃ | Internal Method |
| Vicat Softening Temp | 63.0 | ℃ | ASTM D1525 |
| Melting temperature | |||
| DSC | 77.0 | ℃ | Internal Method |
| Crystallization peak temperature | |||
| DSC | 60.0 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shaw A, molded | 84 | ASTM D2240 | |
| Shaw’s D, molded | 31 | ASTM D2240 | |
| Tensile modulus | |||
| 100% cut, molded | 4.80 | MPa | ASTM D638 |
| tensile strength | |||
| Fracture, molded | 18.2 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, molded | 640 | % | ASTM D638 |
| Bending modulus | ASTM D790 | ||
| 1% cut, molded | 33.7 | MPa | ASTM D790 |
| 2% cut, molded | 32.6 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 20 in/min |
| 3. Die C |
| 4. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |