| ENGAGE™ 8200 Polyolefin Elastomer is an ethylene-octene copolymer that has excellent flow characteristics and performs well in a wide range of general purpose thermoplastic elastomer applications. ENGAGE 8200 provides superb impact properties in blends with polypropylene (PP) and polyethylene (PE), especially in applications requiring slightly higher melt flow. ENGAGE 8200 also provides high filler loading capability, excellent electrical properties, and (when cross-linked) exceptional heat aging, compression set, and weather resistance properties. Main Characteristics: Pellet form Excellent flow characteristics High filler loading Excellent electrical properties Improved impact in polypropylene and polyethylene Exceptional heat aging, compression set, and weather resistance when cured Applications: General purpose thermoplastic elastomers Impact modification Wire and cable&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.870 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 5.0 | g/10min | ASTM D1238 |
| Mooney viscosity | |||
| ML 1+4，121℃ | 8 | MU | ASTM D1646 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | 37.1 | kN/m | ASTM D624 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -53.0 | ℃ | Internal Method |
| Vicat Softening Temp | 37.0 | ℃ | ASTM D1525 |
| Melting temperature | |||
| DSC | 59.0 | ℃ | Internal Method |
| Crystallization peak temperature | |||
| DSC | 44.0 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shore A, 1 second, molded | 66 | ASTM D2240 | |
| Shore D, 1 second, molded | 17 | ASTM D2240 | |
| Tensile modulus | |||
| 100% cut, molded | 2.30 | MPa | ASTM D638 |
| tensile strength | |||
| Fracture, molded | 5.70 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, molded | 1100 | % | ASTM D638 |
| Bending modulus | ASTM D790 | ||
| 1% cut, molded | 10.9 | MPa | ASTM D790 |
| 2% cut, molded | 10.8 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 20 in/min |
| 3. Die C |
| 4. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |