| About |
|---|
| 30% Glass Filled, Amorphous Nylon&& |
| Product Description | |
|---|---|
| Supplier | EnCom |
| Generic | PA Not specified |
| Material Status | Commercial: Active |
| Features | Amorphous |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.46 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 275℃，2.16kg | 40 | g/10min | ASTM D1238 |
| Water absorption rate | |||
| 23℃，24hr，50% RH | 1.1 | % | |
| Saturation, 23 ℃ | 0.14 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 12100 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 179 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.0 | % | ASTM D638 |
| Bending modulus | 11600 | MPa | ASTM D790 |
| bending strength | 286 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 85 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 237 | ℃ | |
| 1.8 MPa, unannealed | 224 | ℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 79 | °C | |
| Drying time | 2.0 to 12 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 25 to 75 | % | |
| Barrel rear temperature | 260 to 282 | °C | |
| Barrel middle temperature | 266 to 288 | °C | |
| Barrel front temperature | 271 to 293 | °C | |
| Nozzle temperature | 271 to 293 | °C | |
| Processing (melt) temperature | 271 to 293 | °C | |
| Mold temperature | 121 to 141 | °C | |
| Back pressure | 0.172 to 0.517 | MPa | |
| Screw speed | 60 to 120 | rpm | |
| Vent depth | 0.025 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |