Ensinger Delrin® AF Blend

About
Ensinger’s DELRIN® 100AF blend stock shapes are a 13% PTFE fiber filled homopolymer acetal. They offer an improved coefficient of friction, better lubricity, and improved wear characteristics over unfilled and PTFE powder filled acetals.This advanced acetal material uses a combination of PTFE fibers uniformly dispersed in Delrin acetal resin. The combination results in improved wear characteristics along with strength, toughness, dimensional stability and machinability. The materials exceptional wear properties and internal lubrication serves to reduce or elimanate the need for external lubricants. Ensinger can also produce a full strength 20% PTFE filled version. DELRIN® 100AF is often used for applications such as bearing, bushings, cams and other antifriction devices that also require extra toughness. Excellent wear characteristics Self lubricating Low coefficient of friction Maximum unmodified toughness Superior load bearing characteristics&&

About

Ensinger’s DELRIN® 100AF blend stock shapes are a 13% PTFE fiber filled homopolymer acetal. They offer an improved coefficient of friction, better lubricity, and improved wear characteristics over unfilled and PTFE powder filled acetals.This advanced acetal material uses a combination of PTFE fibers uniformly dispersed in Delrin acetal resin. The combination results in improved wear characteristics along with strength, toughness, dimensional stability and machinability. The materials exceptional wear properties and internal lubrication serves to reduce or elimanate the need for external lubricants. Ensinger can also produce a full strength 20% PTFE filled version. DELRIN® 100AF is often used for applications such as bearing, bushings, cams and other antifriction devices that also require extra toughness. Excellent wear characteristics Self lubricating Low coefficient of friction Maximum unmodified toughness Superior load bearing characteristics&&

Product Description
Supplier	Ensinger
Generic	Paraformaldehyde
Material Status	Commercial: Active
Features	Good flexibility,Low coefficient of friction,Self-lubricating,Good wear resistance,Homopolymer
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.50	g/cm³	ASTM D792
Water absorption rate
23℃，24hr	0.12	%	ASTM D570

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	53	J/m	ASTM D256

THERMAL	Nominal value	Unit
Hot deformation temperature
0.45 MPa, unannealed	168	℃
1.8 MPa, unannealed	118	℃
Melting temperature	175	℃
Operating temperature
Intermittent	149	℃
long-term	85	℃

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	HB		UL 94

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	79		ASTM D785
Tensile modulus
23℃	2140	MPa	ASTM D638
tensile strength
Yield, 23 ℃	55.8	MPa	ASTM D638
Tensile strain
Yield, 23 ℃	10	%	ASTM D638
Bending modulus
23℃	3340	MPa	ASTM D790
bending strength
23℃	87.6	MPa	ASTM D790
Compression modulus	1720	MPa	ASTM D695
compressive strength
10% strain, 23 ℃	86.2	MPa	ASTM D695

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.