| Ensinger TECARAN™ ABS is a terpolymer and an amorphous resin. It is manufactured by combining three different compounds. The three that make up TECARAN™ ABS are acrylonitrile, butadiene, and styrene. TECARAN™ ABS occupies the unique position of being a bridge between the commodity and other higher performance engineering thermoplastics. Its performance is characterized by toughness and impact strength even at low temperatures, good stiffness and machinability. The applications for TECARAN™ ABS range from Aerospace and automotive parts and housings, to parts for agricultural lawn and garden equipment and components for medical and business equipment, as well as many others. Cost Effective Good Toughness At Low Temperatures Easily Machinable Available In Natural or Black ASTM D 4673 ABS0220B43630 Easily Bonded&& |
| Product Description | |
|---|---|
| Supplier | Ensinger |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,High impact resistance,Machinable,Low temperature toughness,low-temperature impact resistance,Terpolymer,Agglomerability,Amorphous,HB |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Water absorption rate | ASTM D570 | ||
| 23℃，24hr | 0.30 | % | ASTM D570 |
| Saturation, 23 ℃ | 0.70 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23℃ | 340 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 98.9 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 92.2 | ℃ | ASTM D648 |
| Vicat Softening Temp | 104 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 9.4E-5 | 1/℃ | ASTM D696 |
| specific heat | 1170 | J/kg/℃ | |
| Maximum operating temperature | |||
| Intermittent | 99 | ℃ | |
| long-term | 71 | ℃ | UL 746B |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | 18 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 23 ℃，60 Hz | 3.30 | ASTM D150 | |
| Dissipation factor | |||
| 23℃，60 Hz | 0.020 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 102 | ASTM D785 | |
| Tensile modulus | 1860 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 23 ℃ | 35.2 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 15 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 1860 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 55.2 | MPa | ASTM D790 |
| friction coefficient | |||
| With oneself – dynamic | 0.35 | ASTM D1894 | |
| With oneself – static | 0.19 to 0.21 | ||
| Wear factor | |||
| 0.28 MPa，0.25 m/sec | 7100 | 10^-8 mm³/N·m | ASTM D3702 |
| Notes |
|---|
| 1. Natural color only |
| 2. Typical properties: these are not to be construed as specifications. |
| 3. 40 psi, 50 fpm |
| 4. 50% RH |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |