| PA 2202 black is a pigment-filled polyamide 12 powder for manufacturing laser sintered parts that are black throughout. All other part properties are comparable to those of PA 2200. Typical applications for the material are fully functional parts in design quality subject to high mechanical or thermal loads. The parts are black and often look better in technical areas than white parts. As this colour is throughout, scratches or subsequent holes do not degrade the appearance. The parts are also less susceptible to soiling, as soiling is less conspicuous against the black background. The black colour can also be used to differentiate the parts from parts in other colours to prevent confusion.&& |
| Product Description | |
|---|---|
| Generic | PA12 |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | 3D Printing, Laser Sintering/Melting |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.980 | g/cm³ | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 154 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 75.0 | ℃ | ISO 75-2/A |
| Melting temperature | 176 | ℃ | ISO 11357 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 75 | ISO 868 | |
| Tensile modulus | |||
| — | 1850 | MPa | ISO 527-2 |
| — | 1800 | MPa | ISO 527-2 |
| tensile strength | |||
| — | 50.0 | MPa | ISO 527-2 |
| — | 48.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 12 | % | ISO 527-2 |
| fracture | 6.0 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 1350 | MPa | ISO 178 |
| bending strength | 53.0 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Z Direction |
| 3. X Direction |
| 4. Y Direction |
| 5. 20°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |