| About |
|---|
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,High Viscosity,Lubricating,Heat Stabilized |
| Availabilitys | Africa & Middle East ,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| 23℃ | 1.10 | g/cm³ | ISO 1183 |
| water content | 0.1 | % | ISO 15512 |
| Shrinkage rate | 1.4/2 | % | ISO 294-4 |
| MD：3.0 mm | % | ISO 294-4 | |
| TD：3.0 mm | % | ISO 294-4 | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃，1 mm/min | 2400 | MPa | ISO 527-2 |
| 23 ℃, 1 mm/min, pre dried | 1200 | MPa | ISO 527-2 |
| tensile strength | 60 | MPa | ISO 527-2 |
| Fracture, 23 ℃, pre dried | 40 | MPa | ISO 527-2 |
| Tensile strain | >40 | % | ISO 527-2 |
| Fracture, 23 ℃, pre dried | >30 | % | ISO 527-2 |
| bending strength | 2050 | MPa | ISO 178 |
| 23 ℃, pre dried | 900 | MPa | ISO 178 |
| Bending modulus | 85 | MPa | ISO 178 |
| 23 ℃, pre dried | 45 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 13 | kJ/m² | ISO 179-1eA |
| -30℃ | 15 | kJ/m² | ISO 179-1eA |
| -30℃ | 10 | kJ/m² | ISO 179-1eA |
| 12 | kJ/m² | ISO 179-1eA | |
| Notched impact strength of cantilever beam | |||
| 23℃ | NB | kJ/m² | ISO 179/1eU |
| -40℃ | NB | kJ/m² | ISO 179/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| melting point | 220 | ℃ | ISO 3146 |
| Hot deformation temperature | |||
| Hot deformation/B (120 ℃/h-0 45 Mpa) | 160 | ℃ | ISO 75-2/B |
| Hot deformation (120 ℃/h8Mpa) | 60 | ℃ | ISO 75-2/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1E+13 | ohms/sq | ASTM D257 |
| Flammability | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level (0.8mm) | HB | – | EN60695-11-10 |
| Tracking index | 600 | Ω/sq | EN60112 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Dry conditions | Nominal value | Unit | Test method |
| Forming temperature | 220~295 | ℃ | |
| Mold temperature | 90~110 | ℃ | |
| drying temperature | 80~85 | ℃ | |
| Drying time | 4 | H | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |