| A single component, solvent containing, low viscosity polyimide designed for high temperature applications found in semiconductor, hybrid, optical, and medical devices. It is used mostly as a coating and dielectric layer. It can be used at high temperatures. It is a REACH compliant version of EPO-TEK OE132. Formerly 108-43-3&& |
| Product Description | |
|---|---|
| Generic | PI |
| Material Status | Commercial: Active |
| Features | Low Viscosity |
| Availabilitys | Africa & Middle East ,North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| optical performance | Nominal value | Unit | Test method |
| Refractive index | |||
| 589 nm | 1.614 | ||
| Transmittance | |||
| 390-2500 nm | > 70.0 | % | |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Degradation Temperature | 500 | ℃ | |
| working temperature | |||
| Continuous | -55 to 350 | ℃ | |
| Intermittent | -55 to 450 | ℃ | |
| Storage Modulus | 5.52 | GPa | |
| Heating reduction | |||
| 200℃ | 0.15 | % | |
| 250℃ | 0.27 | % | |
| 300℃ | 0.52 | % |
| Uncured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| colour | Yellow | ||
| Density | 1.06 | g/cm³ | |
| viscosity | |||
| 23℃ | 1.2 | Pa·s | |
| Curing time | 2.5 | hr |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 280 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 2.8E-5 | 1/℃ | |
| Storage period | |||
| 23℃ | 52 | wk | |
| drying time | > 7.0 | day |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Below Tg |
| 3. 100 rpm |
| 4. 150°C/1 Hour + 285°C/90 Minutes |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |