| Single component, low viscosity, UV curable epoxy for adhesive sealing and encapsulating fiber optic and optoelectronic packaging application. Replacement version of EPO-TEK OG142-13 with better bonding strength and moisture resistance. Formerly 90-87-6&& |
| Product Description | |
|---|---|
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Low Viscosity,UV Cure |
| Availabilitys | Africa & Middle East ,North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| optical performance | Nominal value | Unit | Test method |
| Refractive index | |||
| — | 1.493 | ||
| — | 1.506 | ||
| Transmittance | |||
| 580-1660 nm | > 97.0 | % | |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Degradation Temperature | 384 | ℃ | |
| Die Shear Strength（>20 kg，23℃） | 46.9 | MPa | |
| working temperature | |||
| Continuous | -55 to 200 | ℃ | |
| Intermittent | -55 to 300 | ℃ | |
| Storage Modulus | 3.59 | GPa | |
| Heating reduction | |||
| 200℃ | 0.32 | % | |
| 250℃ | 0.64 | % | |
| 300℃ | 1.6 | % |
| Uncured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| colour | Clear/Transparent | ||
| Density | 1.17 | g/cm³ | |
| viscosity | |||
| 23℃ | 0.25 to 0.60 | Pa·s |
| Cured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 82 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| — | 5.0E-5 | cm/cm/℃ | |
| — | 1.6E-4 | cm/cm/℃ | |
| Glass transition temperature | > 100 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | |||
| Storage period | 52 | wk |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 3. Below Tg |
| 4. Above Tg |
| 5. 589 nm (uncured) |
| 6. 589 nm (cured) |
| 7. Refrigerated |
| 8. 100 rpm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |