| DESCRIPTION: Epocast® 169A-1 Resin / 9615 Hardener is a two-component, low-density epoxy syntactic which cures at room temperature to a carvable, wood-like product. The cured Epocast® 169A-1 Resin / 9615 Hardener system has good dimensional stability under changing humidity conditions. Epocast® 169A-1 Resin / 9615 Hardener is qualified to SS-9587, Type 1.&& |
| Product Description | |
|---|---|
| Supplier | Huntsman |
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,Machinable,Low density |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | ASTM D1622 | ||
| — | 0.560 | g/cm³ | ASTM D1622 |
| — | 0.680 | g/cm³ | ASTM D1622 |
| — | 0.960 | g/cm³ | ASTM D1622 |
| viscosity | ASTM D2196 | ||
| 25℃ | Paste | ASTM D2196 | |
| 25℃ | Semi-paste | ASTM D2196 | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| compressive strength | 21.4 | MPa | ASTM D695 |
| shear strength | 16.5 | MPa | ASTM D732 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Thermosetting components | |||
| resin | 按重量计算的混合比: 100 | ||
| Hardening method | 按重量计算的混合比: 50 |
| Thermosetting mixed viscosity | Nominal value | Unit | Test method |
|---|---|---|---|
| 25℃ | 35000 | cP | ASTM D2196 |
| Gelation time | |||
| 100 gms，25℃ | 1.0 to 2.0 | hr | ASTM D2471 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Lap Shear（AL/AL） | 8.27 | MPa | ASTM D1002 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Resin |
| 3. System |
| 4. Hardener |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |