| EpoxAmite® White Epoxy Laminating System is an easy-to-use liquid epoxy system formulated for a wide variety of fabrication applications. EpoxAmite® White Laminating System is unfilled, low in viscosity, odorless and cures at room temperature. Cured epoxy displays exceptional physical and performance properties. It can be sanded, shaped, machined, drilled, tapped and painted. EpoxAmite® White Laminating System can be used with reinforcements such as S-Glass, E-Glass, Kevlar and Carbon fibers for lay-up applications or composite parts. EpoxAmite® White Resin can also be mixed with fillers such as fumed silica for gel coat applications. Urefil® 3, Urefil® 7 and other fillers can be added for fairing, filleting or bonding applications.&& |
| Product Description | |
|---|---|
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Blush resistance,Low Viscosity,Sprayable,Machinable,Low odor,Moisture resistance,Room Temperature Cure |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.23 | g/cm³ | ASTM D1475 |
| Specific volume | 0.813 | cm³/g | ASTM D792 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Curing time | 20.0 to 24.0 | hr |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 85 | ASTM D2240 | |
| Tensile modulus | 3840 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 38.6 | MPa | |
| fracture | 212 | MPa | |
| Tensile strain | |||
| fracture | 1.2 | % | ASTM D638 |
| Bending modulus | 3080 | MPa | ASTM D790 |
| bending strength | |||
| — | 218 | MPa | |
| — | 57.6 | MPa | |
| Compression modulus | 786 | MPa | ASTM D695 |
| compressive strength | 82.5 | MPa | ASTM D695 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | 56 | ℃ | ASTM D648 |
| Thermosetting components | |||
| Component A | 按重量计算的混合比: 100 | ||
| Component B | 按重量计算的混合比: 23 | ||
| storage stability | 62 | min | ASTM D2471 |
| Thermosetting mixed viscosity | 2800 | cP | ASTM D2393 |
| working hours | |||
| Thin Film | 2.0 | hr |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 6 ply / 10 oz. laminate after 7 days at 73°F / 23°C |
| 3. 100 g |
| 4. Thin Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |