Eraclene® BB 76

About
Eraclene BB 76 is a high density polyethylene resin (HDPE), with antioxidants, suitable for blow moulding application. It is especially recommended for the production of containers up to 30 liters. Eraclene BB 76 combines an excellent stress cracking resistance with a good rigidity and a high impact strength. For its overall characteristics, Eraclene BB 76 can be used to produce containers able to achieve UN homologation. Main Application Eraclene BB 76 is the ideal resin for packaging of household and industrial chemicals, detergents, fertilizers,adhesives and pesticides. Eraclene BB 76 can be also extruded to obtain profiles and sheets.&&

About

Eraclene BB 76 is a high density polyethylene resin (HDPE), with antioxidants, suitable for blow moulding application. It is especially recommended for the production of containers up to 30 liters. Eraclene BB 76 combines an excellent stress cracking resistance with a good rigidity and a high impact strength. For its overall characteristics, Eraclene BB 76 can be used to produce containers able to achieve UN homologation. Main Application Eraclene BB 76 is the ideal resin for packaging of household and industrial chemicals, detergents, fertilizers,adhesives and pesticides. Eraclene BB 76 can be also extruded to obtain profiles and sheets.&&

Product Description
Generic	HDPE
Material Status	Commercial: Negative
Features	High impact resistance,Food contact compliance,Inoxidizability,High ESCR
Availabilitys	North America,Europe
Process Methods	Profile extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.952	g/cm³	ISO 1183
Melt Flow Rate			ISO 1133
190℃，21.6kg	10	g/10min	ISO 1133
190℃，5.0kg	0.40	g/10min	ISO 1133
ESCR(Environmental Stress Cracking Resistance)
Compression Molding	> 750	hr	ASTM D1693B

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
Compression Molding	250	J/m	ISO 180-A

THERMAL	Nominal value	Unit	Test method
Embrittlement temperature	< -60.0	℃	ASTM D746
Vicat Softening Temp	126	℃	ISO 306/A
Melting temperature	134	℃	Internal Method

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D, molded	65		ISO 868
tensile strength			ISO 527-2
Yield, molding	27.0	MPa	ISO 527-2
Fracture, molded	30.0	MPa	ISO 527-2
Tensile strain
Fracture, molded	> 600	%	ISO 527-2
Bending modulus
Compression Molding	1200	MPa	ISO 178

Process Conditions
Extrusion	Nominal value	Unit	Test method
Barrel 1 zone temperature	180 to 190	°C
Barrel 2 zone temperature	190 to 205	°C
Melt temperature	200 to 210	°C
Nozzle temperature	200 to 210	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.