| Eraclene FC 82 is a high density polyethylene resin (HDPE), with antioxidants, suitable for blown film extrusion. Its broad molecular weight distribution and density successfully combine excellent performance at high extrusion rates with high film strength. Main Application Films produced by Eraclene FC 82 are recommended for high strength grocery sacks, shopping bags, notion and millinery bags. The excellent balance between drawability and bubble stability makes Eraclene FC 82 perfect for manufacturing of high strength thin films (shopping bags, bags on the reel, lamination film).&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Food contact compliance,Inoxidizability,High density |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.953 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，2.16kg | 0.30 | g/10min | ISO 1133 |
| 190℃，21.6kg | 23 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| film thickness | 10 to 50µm | ||
| Tensile modulus | ISO 527-3 | ||
| 1% secant, MD, 25 µ m, blow molded film | 650 | MPa | ISO 527-3 |
| 1% secant, TD, 25 µ m, blow molded film | 800 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, fracture, 25 µ m, blow molded film | 50.0 | MPa | ISO 527-3 |
| TD, fracture, 25 µ m, blow molded film | 45.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 25 µ m, blow molded film | 500 | % | ISO 527-3 |
| TD, fracture, 25 µ m, blow molded film | 650 | % | ISO 527-3 |
| Drop hammer impact | |||
| 25 µ m, blow molded film | 70 | g | ISO 7765-1/A |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD：25.0 µm | 10.0 | kN/m | ISO 6383-2 |
| TD：25.0 µm | 25.0 | kN/m | ISO 6383-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -60.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 127 | ℃ | ISO 306/A |
| Melting temperature | 135 | ℃ | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 190 to 210 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. F50 |
| 3. Blown Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |