| About |
|---|
| FL 00212 is a copolymer of ethylene and vinyl acetate. Processing Conditions Processing temperatures above 260 °C (500 °F) may cause resin degradation. Machines should always be purged with LDPE or a suitable cleaning compound before shutdown.&& |
| Product Description | |
|---|---|
| Supplier | ExxonMobil |
| Generic | EVA |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.5 | g/10min | ASTM D1238 |
| Vinyl acetate content | 12.0 | wt% | ExxonMobil Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 15 seconds | 94 | ASTM D2240 | |
| Tensile modulus | 85.0 | MPa | ASTM D638 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | |||
| 1% secant, TD | 83.0 | MPa | ASTM D882 |
| 1% secant, MD | 78.0 | MPa | ASTM D882 |
| tensile strength | |||
| TD, fracture | 27.8 | MPa | ASTM D882 |
| MD, fracture | 30.4 | MPa | ASTM D882 |
| Tensile strain | |||
| fracture | > 100 | % | ASTM D638 |
| TD, fracture | 660 | % | ASTM D882 |
| MD, fracture | 530 | % | ASTM D882 |
| Drop hammer impact | 480 | g | ASTM D1709-A |
| Elmandorf tear strength | |||
| MD | 110 | g | ASTM D1922 |
| tear strength | |||
| TD | 160 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 70.7 | ℃ | ASTM D1525 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. 20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |