| About |
|---|
| UL 53019CC is a copolymer of ethylene and vinyl acetate.&& |
| Product Description | |
|---|---|
| Supplier | ExxonMobil |
| Generic | EVA |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Vinyl acetate content | 19.0 | wt% | ExxonMobil Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 86 | ASTM D2240 | |
| Tensile modulus | 27.0 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 3.20 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 230 | % | ASTM D638 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Value reported is an estimate based on ExxonMobil’s correlation from melt flow rate data measured at other standard conditions, based on ASTM D 1238. |
| 3. 0.20 in/min |
| 4. 20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |