| About |
|---|
| Escorene Ultra UL 8705 is a relatively low viscosity, 27.6% VA copolymer specifically tailored for enhanced modulus/tensile performance at the same viscosity of similar materials. It has good compatibility with both hydrocarbon and natural tackifiers and most waxes and is suitable for making hot melt adhesives, glue sticks, sealants and wax blends. UL 8705E contains an additive package to improve pellet flowability and handling.&& |
| Product Description | |
|---|---|
| Supplier | ExxonMobil |
| Generic | EVA |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Shore hardness | ASTM D2240 | ||
| Shore A, 15 seconds | 69 | ASTM D2240 | |
| Shore D, 15 seconds | 18 | ASTM D2240 | |
| tensile strength | |||
| fracture | 1.93 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 360 | % | ASTM D638 |
| Bending modulus | |||
| 1% secant | 19.9 | MPa | ASTM D790 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 0.953 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 800 | g/10min | ASTM D1238 |
| Vinyl acetate content | 27.6 | wt% | ExxonMobil Method |
| Apparent viscosity of melt | |||
| 190℃ | 9300 | mPa·s | ASTM D3236 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |