| About |
|---|
| ESPOLEX 817 is a Thermoplastic Polyolefin Elastomer (TPO (POE)) product. It can be processed by blow molding or extrusion and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Applications of ESPOLEX 817 include automotive, hose/tubing and sheet.&& |
| Product Description | |
|---|---|
| Supplier | Sumitomo |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.890 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 1.1 | g/10min | ISO 1133 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 25.0 | MPa | ISO 37 |
| 100% strain | 13.0 | MPa | ISO 37 |
| Tensile strain | |||
| fracture | 820 | % | ISO 37 |
| Compression deformation | |||
| 23℃，22 hr | 56 | % | |
| 70℃，22 hr | 82 | % |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 6.0 | kJ/m² | |
| 23℃ | 无断裂 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | |||
| Type A | -45.0 | ℃ | ISO 812 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 57 | ISO 868 | |
| Bending modulus | 360 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Squeeze description | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 170 to 190 | °C | |
| Barrel 3 zone temperature | 180 to 200 | °C | |
| Barrel 5 zone temperature | 190 to 210 | °C | |
| Nozzle temperature | 200 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type 1A, 20 in/min |
| 3. Type A |
| 4. 3.2 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |