| About |
|---|
| Blend PA/ABS 8% glass fibre reinforced. Exceptional chemical resistance, excellent heat resistance, good dimensional stability. Automotive, motorcycle and cosmetic field. Electronic and electrical, applications. Leisure and household products.&& |
| Product Description | |
|---|---|
| Generic | PA 6+ABS |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,High Heat Resistance,Solvent resistance |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 240℃，10.0kg | 27 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.40 to 0.70 | % | ISO 2577 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3700 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 60.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 3.0 | % | ISO 527-2 |
| Bending modulus | 3500 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 6.0 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| A50 | 190 | ℃ | ISO 306/A50 |
| B50 | 115 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 85 to 90 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Barrel rear temperature | 230 to 240 | °C | |
| Barrel middle temperature | 230 to 250 | °C | |
| Barrel front temperature | 240 to 260 | °C | |
| Nozzle temperature | 240 to 260 | °C | |
| Mold temperature | 50 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |