| About |
|---|
| Type: Estane® 58130 is a 50D Polyester Thermoplastic Polyurethane (TPU). Features: Fast cycling, broad temperature performance, and durability Use: Injection Molding&& |
| Product Description | |
|---|---|
| Supplier | Lubrizol Advanced Materials |
| Generic | TPU-酯 |
| Material Status | Commercial: Active |
| Features | Quick molding cycle,Durability |
| Availabilitys | North America,Latin America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.23 | g/cm³ | ASTM D792 |
| Shrinkage rate | ASTM D955 | ||
| MD | 1.0 | % | ASTM D955 |
| MD | 0.70 | % | ASTM D955 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| Fracture, 0.762 mm | 41.0 | MPa | ASTM D412 |
| 100% strain, 0.762 mm | 11.0 | MPa | ASTM D412 |
| 300% strain, 0.762 mm | 24.0 | MPa | ASTM D412 |
| Tensile strain | |||
| Fracture, 0.762 mm | 450 | % | ASTM D412 |
| tear strength | |||
| 0.762 mm | 137 | kN/m | ASTM D624 |
| cracking | 42 | kN/m | ASTM D470 |
| Compression deformation | ASTM D395 | ||
| 23℃，22 hr | 34 | % | ASTM D395 |
| 70℃，22 hr | 43 | % | ASTM D395 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -40.0 | ℃ | DSC |
| Melting temperature | 218 | ℃ | DSC |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, 5 seconds | 47 to 53 | ASTM D2240 | |
| Bending modulus | |||
| 23℃ | 90.0 | MPa | ASTM D790 |
| Taber abraser | |||
| 1000 cycles, 1000 g, CS-17 wheels | 62.0 | mg | ASTM D3389 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 104 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 204 | °C | |
| Barrel middle temperature | 210 | °C | |
| Barrel front temperature | 218 | °C | |
| Nozzle temperature | 223 | °C | |
| Processing (melt) temperature | 223 | °C | |
| Injection pressure | 69.0 to 103 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Flex Bar |
| 3. Disc |
| 4. Die C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |