ETILINAS BPD 4038

About
ETILINAS BPD 4038 is designed specifically for the jacketing of communication and power cables. It is based on a special high density copolymer with high environmental stress cracking resistance, abrasion resistance, weather resistance and thermal stability. It meets the applicable requirements as below when processed using sound extrusion practice and testing procedure: IEC 708: IEC 6052, ST7; IEC 840; ASTM D1248, Type II, Class C, 5, Grade W6; BS 6234; 03C, TS2.&&

About

ETILINAS BPD 4038 is designed specifically for the jacketing of communication and power cables. It is based on a special high density copolymer with high environmental stress cracking resistance, abrasion resistance, weather resistance and thermal stability. It meets the applicable requirements as below when processed using sound extrusion practice and testing procedure: IEC 708: IEC 6052, ST7; IEC 840; ASTM D1248, Type II, Class C, 5, Grade W6; BS 6234; 03C, TS2.&&

Product Description
Generic	MDPE
Material Status	Commercial: Active
Features	Weather resistance is good,Copolymer,Good wear resistance,Heat Stabilized,High ESCR
Availabilitys	Asia Pacific
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.937	g/cm³	ISO 1183
Melt Flow Rate			ISO 1133
190℃，2.16kg	0.30	g/10min	ISO 1133
190℃，5.0kg	1.3	g/10min	ISO 1133

THERMAL	Nominal value	Unit	Test method
Embrittlement temperature	-100	℃	ASTM D746
Vicat Softening Temp	116	℃	ISO 306/A
Linear coefficient of thermal expansion
MD：20~60℃	1.5E-4	1/℃	ASTM D696

Electrical performance	Nominal value	Unit	Test method
Volume resistivity	1.0E+15	ohms·cm	IEC 60093
Dielectric strength	20	kV/mm	IEC 60243-1
Dielectric constant
1 MHz	2.50		IEC 60250
Dissipation factor
1 MHz	1.0E-3		IEC 60250

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shore D, 1 second	58		ISO 868
Bending modulus	750	MPa	ISO 178

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	200 to 225	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.