| About |
|---|
| ETILINAS LL0209AA is a linear low density polyethylene suitable for a variety of film applications. Characteristics include: low gels content, high strength, and no slip/antiblocking additives. Applications include: sack films, and blown stretchwrap films.&& |
| Product Description | |
|---|---|
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low speed solidification point |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.90 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ISO 527-3 | ||
| MD, yield | 11.0 | MPa | ISO 527-3 |
| TD, yield | 12.0 | MPa | ISO 527-3 |
| MD，38 µm | 40.0 | MPa | ISO 527-3 |
| TD，38 µm | 31.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 38 µ m | 650 | % | ISO 527-3 |
| TD, fracture, 38 µ m | 850 | % | ISO 527-3 |
| Drop hammer impact | |||
| 38 µm | 160 | g | ISO 7765-1 |
| Elmandorf tear strength | |||
| MD，38 µm | 6.0 2.4 | N | ISO 6383-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 100 | ℃ | ISO 306 |
| Melting temperature | |||
| DSC | 122 | ℃ | ISO 3146 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45°，38 µm | 54 | ASTM D2457 | |
| Haze | |||
| 38 µm | 10 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |