| About |
|---|
| The base material for this clear film is amorphous polyphenyl sulphone. It meets FDA and USP requirements making it suitable for food contact and medical applications. In addition to its excellent thermal and mechanical properties, this film is particularly highly resistant to hydrolysis and withstands multiple sterilization by all conventional methods. The transparent material exhibits an exceptionally high refractive index. It can be produced with excellent surface quality to meet demanding optical requirements.&& |
| Product Description | |
|---|---|
| Supplier | Evonik |
| Generic | PPSU |
| Material Status | Commercial: Active |
| Features | Good surface appearance,Good disinfection,Hydrolysis stability,Flame Characteristics,Food contact compliance,Solvent resistance,Amorphous,VTM-0,VTM-1 |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | ISO 1183 |
| dimensional stability | ASTM D1042 | ||
| TD，180℃ | 0.0 | % | ASTM D1042 |
| TD，220℃ | 0.30 | % | ASTM D1042 |
| MD，180℃ | 0.0 | % | ASTM D1042 |
| MD，220℃ | 2.5 | % | ASTM D1042 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 1.1 | % | ISO 62 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Membrane puncture force | |||
| 25 µm | 50.0 | N | |
| 50 µm | 100 | N | |
| 130 µm | 210 | N | |
| tensile strength | ISO 527-3/100 | ||
| Yield, 25 µ m | 70.0 | MPa | ISO 527-3/100 |
| Yield, 50 µ m | 75.0 | MPa | ISO 527-3/100 |
| Yield, 130 µ m | 75.0 | MPa | ISO 527-3/100 |
| Yield, 250 µ m | 75.0 | MPa | ISO 527-3/100 |
| 25 µm | 70.0 | MPa | ISO 527-3/100 |
| 50 µm | 75.0 | MPa | ISO 527-3/100 |
| 130 µm | 80.0 | MPa | ISO 527-3/100 |
| 250 µm | 80.0 | MPa | ISO 527-3/100 |
| Tensile strain | ISO 527-3/100 | ||
| Fracture, 25 µ m | 25 | % | ISO 527-3/100 |
| Fracture, 50 µ m | 90 | % | ISO 527-3/100 |
| Fracture, 130 µ m | > 100 | % | ISO 527-3/100 |
| Fracture, 250 µ m | > 100 | % | ISO 527-3/100 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 222 | ℃ | ISO 306/B |
| Operating temperature | 190 | ℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.13 mm | VTM-1 | UL 94 | |
| 0.05 mm | VTM-0 | UL 94 | |
| Smoke Toxicity | Pass | AITM 3.0005 | |
| Smoke density | Pass | AITM 2.0007 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.675 | ISO 489 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| OSU Test | |||
| HR：250.0 µm | 16.0 | kW·min/m² | FAR 25.853(d |
| HRR：250.0 µm | 12.0 | kW/m² | AITM 2.0006 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |