| 38 mol% Ethylene Vinyl Alcohol Copolymer H171B – Pellets are lubricated to facilitate material feeding into extruder&& |
| Product Description | |
|---|---|
| Generic | EVOH |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，2.16kg | 1.7 | g/10min | ISO 1133 |
| 210℃，2.16kg | 3.4 | g/10min | ISO 1133 |
| Ethylene composition | 38.0 | wt% | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Oxygen permeability | ISO 14663-2 | ||
| 20℃，0% RH | 0.012 | cm³·mm/m²/atm/24 hr | ISO 14663-2 |
| 20℃，65% RH | 0.014 | cm³·mm/m²/atm/24 hr | ISO 14663-2 |
| 20℃，85% RH | 0.044 | cm³·mm/m²/atm/24 hr | ISO 14663-2 |
| Water vapor transmittance | |||
| 40℃，90% RH | 0.94 | g·mm/m²/atm/24 hr | ASTM E96 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | 2.0 | kJ/m² | ISO 179/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 53.0 | ℃ | ISO 11357-2 |
| Melting temperature | 172 | ℃ | ISO 11357 |
| Crystallization peak temperature | 148 | ℃ | ISO 11357-3 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 85 | ISO 2039-2 | |
| Tensile modulus | 2600 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 27.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 15 | % | ISO 527-2 |
| Bending modulus | 4800 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Procedure E |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |