| About |
|---|
| EVATANE® 28-05 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerization process. The high Vinyl Acetate content of EVATANE® 28-05 brings softness, flexibility and polarity. EVATANE® 28-05 is compatible with most tackifying resins and waxes and is an efficient and easy handling product for hot melt adhesives formulations. EVATANE® 28-05 delivers high cohesive strength with most fillers and may be used to produce masterbatches, HFFR compounds and foams. EVATANE® 28-05 is also suitable for film (cast or blown) extrusion, and exhibits good adhesion onto PE, PS and polyesters.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | EVA |
| Material Status | Commercial: Active |
| Features | Good flexibility,Good bond,Random copolymer,Soft |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.950 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 5.0 to 8.0 | g/10min | ASTM D1238 |
| 190℃，2.16kg | 5.0 to 8.0 | g/10min | ISO 1133 |
| Vinyl acetate content | 27.0 to 29.0 | wt% | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 80 | ISO 868 | |
| Shaw’s A | 80 | ASTM D2240 | |
| tensile strength | |||
| fracture | 24.0 | MPa | ISO 527-2 |
| fracture | 24.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 700 to 1000 | % | ASTM D638 |
| fracture | 700 to 1000 | % | ISO 527-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 40.0 | ℃ | ASTM D1525 2 |
| Vicat Softening Temp | 40.0 | ℃ | ISO 306/A |
| Melting temperature | 72.0 | ℃ | ISO 11357-3 |
| Ring and Ball Softening Point | 160 | ℃ | ASTM E28 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 3. NF EN 1238 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |