| About |
|---|
| EVATANE® 28-420 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerization process. The high Vinyl Acetate content of EVATANE® 28-420 brings softness, flexibility and polarity. EVATANE® 28-420 is compatible with most tackifying resins and waxes. Combined with a high fluidity, it is an efficient and easy handling product for hot melt adhesives formulations.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | EVA |
| Material Status | Commercial: Active |
| Features | Good flexibility,Random copolymer,Soft |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.950 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 370 to 470 | g/10min | ASTM D1238 |
| 190℃，2.16kg | 370 to 470 | g/10min | ISO 1133 |
| Vinyl acetate content | 27.0 to 29.0 | wt% | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 70 | ISO 868 | |
| Shaw’s A | 70 | ASTM D2240 | |
| tensile strength | |||
| fracture | 5.00 | MPa | ISO 527-2 |
| fracture | 5.00 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 400 to 600 | % | ASTM D638 |
| fracture | 400 to 600 | % | ISO 527-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | < 40.0 | ℃ | ASTM D1525 2 |
| Vicat Softening Temp | < 40.0 | ℃ | ISO 306/A |
| Melting temperature | 66.0 | ℃ | ISO 11357-3 |
| Ring and Ball Softening Point | 84 | ℃ | ASTM E28 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 3. NF EN 1238 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |